internal shrinkage

英 [ɪnˈtɜːnl ˈʃrɪŋkɪdʒ]

美 [ɪnˈtɜːrnl ˈʃrɪŋkɪdʒ]

网络  内缩孔

机械

双语例句

• The final hanger force is mostly related to deadweight of the girder, and affected by the internal force redistribution caused by prestressing reinforcements, shrinkage and creep of concrete.
  成桥索力主要与恒载有关，同时边跨预应力引起的内力重分布以及混凝土的收缩徐变都会对成桥索力产生影响。
• The casting is easy to suffer from deformation, surface sink and internal shrinkage.
  该铸件容易变形和产生表面缩凹、部缩孔。
• This paper mainly studies the redistribution of internal force of the steel-concrete composite structure due to concrete shrinkage and creep, and the calculation method for construction simulation.
  主要研究了混凝土收缩徐变引起的钢与混凝土组合结构的内力重分布及施工模拟计算方法。
• Ingot defects may be broadly classified into internal flaws and surface flaws. Internal flaws are caused by shrinkage.
  钢锭缺陷广义上可分为内部缺陷和表面缺陷。内部缺陷是因收缩引起的。
• Internal force effects in a component due to creep and shrinkage shall be considered.
  应考虑在一构件内由于徐变和收缩引起的内部力效应。
• It may help the readers to understand the computational principle of secondary internal forces due to the creep and shrinkage of concrete.
  它将有助于读者对混凝土徐变和收缩次内力计算原理的理解。
• There easily exists shrinkage porosity due to superheat of ingate root in large plain parts investment casting. Ingot defects may be broadly classified into internal flaws and surface flaws. Internal flaws are caused by shrinkage.
  大平面铸件常在内浇道根部出现过热，在该处产生缩松缺陷。钢锭缺陷广义上可分为内部缺陷和表面缺陷。内部缺陷是因收缩引起的。
• Beam-column effect, large deflection effect, elongation of the cable and the other geometrical nonlinearity and structural secondary internal forces which causes from the prestress, the creep and shrinkage of concrete and the temperature in the mechanical model are inducted.
  其中，在建模中考虑的主要因素是：梁柱效应、大变形效应、斜拉索垂度等几何非线性，预应力、混凝土收缩徐变、温度等引起的结构次内力；
• Experimental study on internal defect of heavy section shrinkage workpiece under one cross wedge rolling
  大断面收缩率一次楔入轧件心部缺陷的实验研究
• The shrinkage defects in Mg alloy die casting were examined. Occurrence of surface and internal fissure was attributed to delamination filling during the ejection of diecasting with the asynchronism of the solidification shrinkage.
  对音箱面板镁合金压铸件出现的收缩缺陷进行了检测分析，认为表面裂痕和内部裂纹产生的原因是由于压铸喷射填充状态下的分层充填以及凝固收缩的不同时性所引起的；